Description
- high-quality adhesive based on MS polymers
- for bonding metals, wood and plastics to and among each other in body and vehicle construction, container construction, sheet metal processing, apparatus engineering, air conditioning, yacht u. boat building
- Elastic sealing of seams
- In areas where silicone cannot be processed. (silicone contamination when painting)
- Permanently elastic adhesive
- high strength
- Re-coatable with dispersion paints (alkyd paints may have a delayed drying time, test before)
- suitable for wet use
- Resistant to UV, weather, (salt)water, moisture and chlorine, anti-fungal
- No edge zone contamination (very suitable for natural stone)
- very good adhesion on many substrates
- Free of isocyanate, solvents, phthalate and silicone
- colour-tight
- Odourless
- Sandable (after hardening)
- Very good adhesion to many substrates, in most cases without adhesive primer
(for porous substrates, test in advance) - ISEGA certificate no. 43705 U 16
- colour: white
- Viscosity: pasty
- max. joint width: 25 mm
- density: 1.532 g/ml
- Hardening in 24 hours: 3.0 mm
- Shrinkage: none
- Skin formation (23 °C / 55 % RF): approx. 10-15 minutes
- Break elongation (DIN 53504): 300%
- E-type at 100% expansion (DIN 53505): 1.7 MPa
- Hardness Shore A (DIN 53505): 60
- temperature resistance: -40 °C to +100 °C, short-term up to +130 °C
- Processing temperature 5 – 30 °C
- Processing time: 10 min
Technical data
Gross weight | 140 g |